Genleşmiş Perlitin Soğuk Vulkanize Yapıştırıcıların Vulkanizasyon Karakteristikleri ve Mekanik Özellikleri Üzerine Etkisi

Abstract

In rubber industry, incorporation of various reinforcing fillers is a widespread procedure to enhance the properties of the material or save costs. In this study, expanded perlite was used as a new type of filler for cold vulcanizing adhesives. Perlite‐filled rubber blends were prepared using a laboratory sized tworoll mill. Influences of expanded perlite loading compared with commercial calcite were investigated on cure characteristics and mechanical properties, such as adhesive strength and hardness. The crosslink density was also determined in both samples by means of swelling in solvent. The addition of perlite as filler showed a decrease in scorch time (tS2) and cure time (t90), an increase in mechanical properties and crosslink density. The results show that expanded perlite can be used as filler in cold vulcanizing adhesive formulation.

Kauçuk endüstrisinde, ürün özelliklerinin iyileştirilmesi ve maliyeti düşürmek amacıyla çeşitli kuvvetlendirici dolgu maddeleri yaygın olarak kullanılmaktadır. Bu çalışmada, soğuk vulkanize yapıştırıcıların üretiminde yeni bir dolgu maddesi olarak genleşmiş perlit kullanılmıştır. Perlit dolgulu kauçuk karışımları laboratuvar ölçekli iki silindirli mil kullanılarak hazırlanmıştır. Genleşmiş perlitin vulkanizasyon karakteristiği ve mekanik özellikleri (yapışma direnci ve sertlik vb. ) üzerine etkileri ticari dolgu maddesi olarak kullanılan kalsit ile karşılaştırılarak araştırılmıştır. Her iki numunenin solvent içerisinde şişirilmesiyle çapraz bağ yoğunluğu belirlenmiştir. Dolgu olarak perlit kullanımı ile scorch süresi (ts2) ve vulkanizasyon süresinde (t90) azalma, çapraz bağ yoğunluğunda artma ve mekanik özelliklerinde iyileşme gözlenmiştir. Deneysel sonuçlar, genleşmiş perlitin soğuk vulkanize yapıştırıcı formülasyonlarında dolgu maddesi olarak kullanılabileceğini göstermiştir